Thermosetting ink for touch screen application
Resist ink with flexibility and adhesion. Regardless of resistive touch screen or capacitive touch screen,it has good usage record as overcoat material.
Product | Outline | colour | Total Transmittance | Haze | Viscosity (at 25 ℃) (VT-06) | Curing conditions |
CR-18T-KT1 | 2 component type,Thick film coating is possible | milky white | ≧90% | ≧70% | 40-70 dPa・s | 130℃×10min |
Thermosetting High Transparency ink for touch screen application
Excellent transparency, not only suitable for use as frame circuit protection, but also in application to view area.
Product | Outline | Colour | Total Transmittance | Haze | Viscosity (at 25 ℃) | Curing conditions |
FR-1T-NSD9 | 2 component type, High transparency, High smoothness | Slightly muddy, transparent | ≧99% | Approx. 0.2% | 20-60 dPa・s (B-8U) | 110℃×30min |
FR-1T-NSD12L | 2 component type, High transparency, High smoothnes | Slightly muddy, transparent | ≧99% | Approx. 0.2% | 60-100 dPa・s (TVB-10) | 110℃x30min |
UV curing type ink for touch screen application
It has good usage record as overcoat for touch screen that cannot be subjected to heat, and as Dot-spacer for resistive touch screen.
Product | Outline | Colour | Viscosity (at 25 ℃) (VT-06) | UV Exposure |
UVF-10T-DS | 1 component type,For Dot-spacer application, Fine pattern, Thick film | Milky white | 900-1300 dPa・s | ≧ 1000 mJ/cm2 |
UVF-DS3 | 1 component type, For Dot-spacer application, High strength | Milky white | 750-950 dPa・s | ≧ 600 mJ/cm2 |
UVF-10T(KAI) | 1 component type, General-purpos | Milky white | 100-200 dPa・s | ≧ 800 mJ/cm2 |
UVF-31T | 1 component type, High adhesion | Milky white | 400-600 dPa・s | ≧ 800 mJ/cm2 |
Thermosetting resist ink for electro-less Ni/Au plating
Highly reliable plating resist which has low elution and contamination to plating solution.
We have a variety of products from FPC applicable types to low-odor types.
Product | Outline | Colour | Flexibility | Viscosity (at 25 ℃) | Curing conditions |
MR-303F | 1 component type, Added flexibility,Low contaminaton to electroless plating solution | Black | Moderate | 100-200 dPa・s (VT-06) | 100℃×10min |
MR-303FTHV1 | High viscosity and color free type of MR-303F | Milky white | Moderate | 300-500 dPa・s (VT-06) | 100℃×10min |