Carbon paste for PTF Conductor on rigid / flexible board
Carbon paste series available for resistance, key contact / cross over circuit.
Product | Outline | Adjust resistivity | viscosity (at 25℃) | Curing conditions |
TU-○○-8 | Carbon conductive paste for fixed resistance | 100Ω 1kΩ | 500-700 dPa･s | 170℃×60min |
10kΩ 100kΩ | ||||
/□/14μm(film thickness) | ||||
BTU-○○-10 | Carbon conductive paste for sliding resistance | 100Ω 1kΩ | 400-500 dPa･s | 170℃×60min |
10kΩ 100kΩ | ||||
/□/15μm(film thickness) |
＊”○○” is used for resistance value. ex. 100Ω type TU-100-8
Silver paste for touch screen, membrane circuit.
Application to ITO-PET film is possible. Wide array of usage purposes such as touch screen switch, membrane circuit formation, and EL element application.
Product | Outline | Printability | Sheet resistivity （Film thickness 10μm） | Viscosity (at 25℃) | Curing conditions |
LS-450-5 | For fine printing application, good adhesion to various kinds of ITO | 70-80 μm | 65mΩ/□ | 600-800 dPa･s | 130℃×30min |
LS-450-7H | For fine printing application, good adhesion to thin film type ITO | 50-60 μm | 80mΩ/□ | 1100-1400 dPa･s | 130℃×30min |
LS-460H-1 | For fine printing application, great with various screens
| 50 μm | 90mΩ/□ | 1200-1800 dPa･s | 130℃×30min |
LS-453-1 |
Low temperature curing type
| 80-100 μm | 50mΩ/□ | 350-450 dPa･s | 100℃×30min |
Ag paste for laser cutting process
Product | Outline | Workability | Sheet resistivity （Film thickness 10μm） | viscosity (at 25℃) | Curing condition |
LS-470L-2 | General-purpose product | 30/30 μm | 85mΩ/□ | 350-450 dPa･s | 130℃×30min |
SNP-120L | General-purpose, Large particle reduced product | 20/20 μm | 60mΩ/□ | 350-450 dPa･s | 130℃×30min |
SNP-210L | Lowes-cost, Large particle reduced product | 20/20 μm | 70mΩ/□ | 200-400 dPa･s | 130℃×30min |
| SNP-300L-SP2 | Low temperature curing, Large particle reduced product | 20/20 μm | 70mΩ/□ | 350-450 dPa･s | 80℃×30min |